Designed for printing models that have high requirements in mechanical properties. Durable, non-shrinking and odorless
Designed for printing models that have higher requirements for mechanical properties. Durable, non-shrinking and odorless.
The fully cured polymer is very hard and elastic the same time. This allows you to print functional parts that can withstand mechanical stress.
Cured models are resistant to decay and can withstand high temperatures (up to 100 ° C), which makes it possible to use models to create silicone molds by cold and hot vulcanization. Works with two-component silicone on tin catalysts.
The resin has relatively low viscosity. It decreases time for levelling, easy to clean to provide maximum accuracy at minimum time.
Resins are odorless and cause no irritation, so you can work with natural ventilation without special technique.
Shrinkage less than 0.5% gives you the same size like 3D model on your computer and it doesn’t change size after postcuring.
Resin does not contain solvents and volatile monomers, irritating compounds. No fumes, odor and allergic reaction
Hard but Tough
Resins have 85-92 Shore D hardness the same time elastic. These unique properties are very useful in printing durable non-brittle models, you can use master-models for casting in rubber several times
Resin is very stable, you can leave it for a long time in the vat, no sedimentation and gel formation occur – no need to mix even pigment containing resins such as White, Black, Blue, Grey
Models has long-term stability under 100*C that make possible to cast it in cold and hot silicone or 2k resin molds. Also has short-term stability up to 180*C and models can be used for films thermosettling
Very wide color choice gives an advantage to the customer. Clear and White resins are specially for DIY tinting so you can easily get your own color shade.
|Appearance||Colored transparent liquid|
|Color||Clear, Natural Clear, Grey, Black, White, Cherry, Blue|
|Viscosity according to Brookfield||0.8-1 Pa*s|
|Tensile strength||45 N/mm2|
|Elongation at break||4-6%|
|Hardness Shore D||87-92|